Coating compositions, process and luminescent coated articles

ABSTRACT

The invention is directed to a composition having a carrier matrix, and a particulate luminescent composition dispersed therein, the particulate luminescent composition comprising a rare-earth-doped solid-state solution of alkaline earth fluorides represented by the chemical formula 
       RE x (Ca a Sr b Ba c ) 1−x F 2+x−2y O y            wherein RE represents a three-valent rare-earth element, 0.005≦x≦0.20, and 0≦y≦0.2, a+b+c=1, with the proviso at least two of a, b, and c are not equal to zero; the particulate luminescent composition exhibiting a luminescence spectrum having a plurality of intensity peaks at characteristic wavelengths. It is further directed to a process by contacting a surface with the composition and articles made therefrom.

FIELD OF THE INVENTION

The present invention is directed to coating compositions, such as inks, paints, etc, that provide luminescent coatings on an article. The luminescent species is a rare-earth doped solid state solution of alkaline earth fluoride. The invention is useful for providing identifying markers on articles. Other uses include the preparation of phosphors for plasma displays.

BACKGROUND OF THE INVENTION

Luminescent rare-earth doped alkaline-earth fluorides have long been known, and have been employed for numerous purposes such as scintillation detectors and laser materials. CaF₂ doped with such rare-earth species as Eu⁺³, Er⁺³, Tb⁺³ are well-known compositions. It is well-known that a rare-earth doped alkaline earth fluoride will exhibit luminescence when exposed to ultraviolet light.

Each rare-earth element when incorporated into an alkaline earth host lattice such as CaF₂ exhibits a characteristic excitation spectrum; see, for example, FIG. 1 (101), and a characteristic emission or luminescence spectrum that depends upon the excitation wavelength employed; see, for example, FIG. 1 (102). The excitation spectrum is determined by monitoring the luminescence intensity at one wavelength while the specimen is illuminated over a range of wavelengths. The luminescence spectrum is determined by illuminating the specimen at a single wavelength corresponding to a peak in the excitation spectrum and determining the luminescence spectrum by scanning a detector over a range of wavelengths.

As shown in the FIGURE, each such spectrum consists of a plurality of peaks at different wavelengths of light. The wavelengths at which the peaks occur are characteristic of each rare-earth element. No two rare-earth elements exhibit the same excitation or emission spectra; that is, the peaks in their spectra do not in general arise at the same wavelengths. To obtain luminescence, the rare-earth element must be excited by a light source that emits light at a wavelength corresponding to the location of one of the peaks in the excitation spectrum thereof. In general, the peaks in any one spectrum of rare-earth elements differ from one another in height or intensity, these differences in intensity being characteristic of the rare-earth element under particular conditions of measurement. These and related matters are all well-documented in the art. See for example, Martin et al., Atomic Energy Levels—the Rare-Earth Elements, U.S. Department of Commerce, National Bureau of Standards (1978).

Haubold et al., U.S. Published Patent Application 2003/0032192 discloses the use of doped luminescent inorganic compounds for marking goods, such as in use as so-called anti-theft or anti-counterfeiting security markers. Use of rare-earth doped alkaline earth fluorides is not disclosed.

Gardner et al., U.S. Pat. No. 6,861,012, discloses use of phosphorus-based inorganic chelates that are “cropped to” polymer particles employed in ink jet printing inks to provide UV-activated luminescence for marking goods. There is no disclosure of rare-earth doped alkaline earth fluoride compositions.

Sarma et al., Solid State Ionics 42, 227 (1990) discloses solid state solutions of CaF₂ and SrF₂. No mention is made of rare-earth doping.

Federov et al., Doklady Akademii Nauk. 369(2):217-219, 1999, discloses solid solutions consisting of a series of 10 mm diameter and 50 mm long single crystals of (Ca_(1−y)Sr_(y))_(1−x)Nd_(x)F_(2+x) grown by the Bridgman-Stockbarger method by crystallization from the melt.

Considerable effort in the art is being directed towards developing luminescent compositions for use as identifying marks on commercial goods, including packages, manufactured articles, and even money. One idea is to place an identifying mark on a manufactured article which will attest to its authenticity in the face of rampant piracy on a global scale. The mark is ideally invisible until inquiry is made using a particular wavelength of light which then stimulates luminescence with a characteristic spectrum.

A simple luminescent security mark may itself be easy to counterfeit. In the present invention a family of novel rare-earth-doped alkaline earth fluorides, and a process for preparing them, that are characterized by unique luminescence peak intensity ratios, making it extraordinarily difficult to counterfeit security marks comprising these compositions.

SUMMARY OF THE INVENTION

The present invention provides a composition comprising a carrier matrix, and a particulate luminescent composition dispersed therein, the particulate luminescent composition comprising a rare-earth-doped solid-state solution of alkaline earth fluorides represented by the chemical formula

RE_(x)(Ca_(a)Sr_(b)Ba_(c))_(1−x)F_(2+x−2y)O_(y)

wherein RE represents a three-valent rare-earth element, 0.005≦x≦0.20, and 0≦y≦0.2, a+b+c=1, with the proviso at least two of a, b, and c are not equal to zero; the particulate luminescent composition exhibiting a luminescence spectrum having a plurality of intensity peaks at characteristic wavelengths.

Further provided is a process comprising contacting a surface with a composition comprising

a carrier liquid and a particulate luminescent composition dispersed therein, the particulate luminescent composition comprising a rare-earth-doped solid-state solution of alkaline earth fluorides represented by the chemical formula

RE_(x)(Ca_(a)Sr_(b)Ba_(c))_(1−x)F_(2+x−2y)O_(y)

wherein RE represents a three-valent rare-earth element, 0.005≦x≦0.20, and 0≦y≦0.2, a+b+c=1, with the proviso at least two of a, b, and c are not equal to zero; the particulate luminescent composition exhibiting a luminescence spectrum having a plurality of intensity peaks at characteristic wavelengths, thereby forming upon the surface a coating comprising the composition.

Further provided is an article having a surface, the surface having disposed upon it a coating comprising a particulate luminescent composition dispersed therein, the particulate luminescent composition comprising a rare-earth-doped solid-state solution of alkaline earth fluorides represented by the chemical formula

RE_(x)(Ca_(a)Sr_(b)Ba_(c))_(1−x)F_(2+x−2y)O_(y)

wherein RE represents a three-valent rare-earth element, 0.005≦x≦0.20, and 0≦y≦0.2, a+b+c=1, with the proviso at least two of a, b, and c are not equal to zero, the particulate luminescent composition exhibiting a luminescence spectrum having a plurality of intensity peaks at characteristic wavelengths.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is an excitation spectrum of Eu_(0.05)Ca_(0.95)F_(2.05−2y)O_(y). observed at 591 nm and a luminescence spectrum of Eu_(0.05)Ca_(0.95)F_(2.05−2y)O_(y) excited at 394 nm.

DETAILED DESCRIPTION

The present invention provides a composition comprising a carrier matrix, and a particulate luminescent composition dispersed therein, the particulate luminescent composition comprising a rare-earth-doped solid-state solution of alkaline earth fluorides represented by the chemical formula

RE_(x)(Ca_(a)Sr_(b)Ba_(c))_(1−x)F_(2+x−2y)O_(y)

wherein RE represents a three-valent rare-earth element, 0.005≦x≦0.20, and 0≦y≦0.2, a+b+c=1, with the proviso at least two of a, b, and c are not equal to zero; the particulate luminescent composition exhibiting a luminescence spectrum having a plurality of intensity peaks at characteristic wavelengths.

It is a characteristic of the rare-earth-doped solid-state solution of alkaline earth fluorides employed herein that at least one pair of said luminescence peaks exhibits an intensity ratio with respect to one another that differs by at least 5% from the corresponding intensity ratio of a corresponding reference composition.

For the purpose of the present invention the term “solid state solution” is employed to refer to a composition such as but not limited to Sr/CaF₂:EuF₃, that forms a single crystalline phase as indicated by x-ray diffraction (XRD) analysis whereas a simple mixture of, e.g., a SrF₂:EuF₃ and a CaF₂:EuF₃ is shown by XRD to consist of multiple crystalline phases.

The rare-earth doped solid state solutions of alkaline earth fluorides suitable for use in the present invention may conveniently be prepared according to the precipitation process and, if desired, the heating process described, infra. However, the composition hereof is not limited in scope to any particular means of preparation for the rare-earth doped solid state solutions of alkaline earth fluorides. For the purposes of the present invention, the process by which the composition is synthesized shall be known as the “precipitation process.” Any embodiment of the rare-earth doped composition suitable for use herein that has not been exposed to a temperature above 100° C. shall be referred to as an “as-precipitated” embodiment regardless of whether that embodiment was actually prepared by precipitation.

The rare-earth doped solid state solution of alkaline earth fluorides suitable for use herein has many embodiments that differ from one another, inter alia, by virtue of the particular rare-earth, and the particular alkaline earth cations incorporated therein, as well as by the relative amounts thereof, that is, by the values of x, a, b, and c. To each said rare-earth doped solid state solution of alkaline earth fluorides suitable for use herein there corresponds a so-called “reference composition.” The reference composition is a solid state solution consisting of the same rare-earth and alkaline earths in the same relative amounts as that suitable or use herein to which it corresponds; that is, RE, x, a, b, and c are the same as in that of the rare-earth doped solid state solution of alkaline earth fluorides suitable for use herein to which the reference composition corresponds. However, unlike the rare-earth doped solid state solution of alkaline earth fluorides suitable for use herein, that can be prepared according to the process described infra, the reference composition is prepared by crystallization from the melt in the manner of Federov, op. cit. Each rare-earth doped solid state solution of alkaline earth fluorides suitable for use herein, and each reference composition corresponding thereto, is characterized by a luminescence spectrum having a plurality of luminescence peaks at characteristic wavelengths. Any pair of said plurality of luminescence peaks is characterized by the ratio of the intensities (or heights) thereof. According to the present invention, for each rare-earth doped solid state solution of alkaline earth fluorides suitable for use herein, there is at least one pair of said plurality of peaks whereof the ratio of said intensities (or intensity ratio) differs by at least 5% from the intensity ratio of peaks at the same wavelengths in the luminescence spectrum of the corresponding reference composition.

The particulate luminescent compound suitable for use in the present invention comprises the rare-earth doped solid state solution of alkaline earth fluorides suitable for use herein. The rare-earth doped solid state solution of alkaline earth fluorides suitable for use herein is itself particulate in nature as well as luminescent. However, as described infra, the particulate luminescent composition suitable for use in the present invention may include additional materials.

The rare-earths suitable for the practice of the invention include all the members of the Lanthanide series in the periodic table of the elements with the exception of promethium and lutetium. The rare-earth elements are all in the +3-valent state. Eu+3, Er+3, and Tb+3 are preferred.

In a further embodiment 0.01≦x≦0.10.

In another embodiment, one of a, b, or c=0. In a still further embodiment, a=0.01 to 0.99, b=0.99 to 0.01, and c=0. In a further embodiment, a=0.25 to 0.75 and b=0.75 to 0.25, while c=0.

In a further embodiment, RE is Eu+3, Er⁺³, or Tb⁺³, 0.01≦x≦0.10, a=0.01 to 0.99, b=0.99 to 0.01, and c=0, In a still further embodiment 0.02≦x≦0.10.

In another embodiment, the present invention encompasses compositions comprising a rare-earth doped solid state solution of alkaline earth fluorides represented by the formula

RE_(x)(Ca_(a)Sr_(b)Ba_(c))_(1−x)F_(2+x−2y)O_(y)

wherein RE represents a three-valent rare-earth element, 0.005≦x≦0.20, and 0≦y≦0.2, a+b+c=1, with the proviso at least two of a, b, and c are not equal to zero; the rare-earth doped multi-valent metal fluoride being characterized by an aqueous solubility of less than 0.1 g/100 g of water.

The particulate luminescent composition suitable for use in the present invention is not limited to any particular method by which it is prepared. One method for preparing the rare-earth doped solid state solution of alkaline earth fluorides suitable for use herein is a process comprising combining an aqueous solution of ammonium fluoride with one or more aqueous solutions of the salts of at least two alkaline earth metals, and an aqueous solution of a salt comprising a 3-valent rare earth metal cation, the amount of the rare-earth metal cation being in the range of 0.5 to 20 mol-% of the molar concentration of the total alkaline earth metal cation content, thereby forming a reaction mixture from which is formed a precipitate of a rare-earth doped solid state solution of alkaline earth fluorides represented by the formula

RE_(x)(Ca_(a)Sr_(b)Ba_(c))_(1−x)F_(2+x−2y)O_(y)

wherein RE represents a three-valent rare-earth element, 0.005≦x≦0.20, and 0≦y≦0.2, a+b+c=1, with the proviso at least two of a, b, and c are not equal to zero; the rare-earth doped multi-valent metal fluoride being characterized by an aqueous solubility of less than 0.1 g/100 g of water.

The reaction in aqueous solution of the soluble fluoride with the soluble alkaline earth salts and rare earth salt is very rapid. Precipitation occurs so quickly in the process of the invention that there is little time for crystal growth after nucleation, except in highly dilute solution.

The particles produced according to the present invention comprise a crystalline or semi-crystalline host material and a dopant. The host material is a solid state solution of at least two alkaline earth fluorides characterized by an aqueous solubility of less than 0.1 g/100 g of water. The dopant is a three-valent rare-earth cation which occupies specific lattice sites in the crystalline structure of the host material.

In the process for preparing the rare-earth doped solid state solution of alkaline earth fluorides suitable for use herein an aqueous solution of ammonium fluoride is combined with one or more aqueous solutions of the salts of at least two alkaline earth metals, and an aqueous solution of a rare earth metal salt. The aqueous solubility of the resulting rare-earth doped solid state solution of two or more alkaline earth fluorides is less than 0.1 g/100 g at room temperature.

The term “rare-earth” refers to the members of the Lanthanide Series in the periodic table, namely La, Ce, Pr, Nd, Sm, Eu, Gd, Tb, Dy, Ho, Er, Tm, and Yb.

Preferred anions for the soluble alkaline earth metal salt include chloride, nitrate, sulphate, hydroxide, acetate, carbonates, phosphates, bromides, and hydrates thereof.

The process herein can be employed to make both nano-sized particles and micro-sized particles, depending upon the reaction conditions. For the purpose of the present invention, the term “nano-sized” shall be understood to refer to a batch of particles of which fewer than 50%, preferably fewer than 90%, of the particles by weight are trapped in a 200 nm filter. It has been found in the practice of the invention that a 0.2 micrometer Zapcap-CR chemically resistant bottle top filter available from Schleicher & Schueel Microscience, is satisfactory for this determination.

For the purpose of the present invention, the term micro-sized shall be understood to refer to a batch of particles of which at least 50%, preferably at least 90%, of the particles by weight are trapped in a 500 nm filter. Particles said to be micro-sized shall be further characterized in that fewer than 50%, preferably fewer than 90%, of the particles by weight are trapped in a 200 micrometer filter.

Soluble salt starting materials need only be soluble enough to form aqueous solutions of the desired concentrations for the purposes of the present invention. A salt is, for the purposes herein, said to be aqueously soluble if a solution of the desired concentration can be formed from it.

Three processes are involved in the precipitation of a solid product from a homogenous reaction solution. (1) chemical reactions that produce supersaturation, (2) nucleation of particles and (3) and growth of particles. For fast reactions, such as occur herein, small particles are produced when there is a localized high concentration of the crystallizing species in solution and high supersaturation, which results in high nucleation rates, high nuclei densities, and low growth rates. Large particles are produced by reducing the local solution supersaturation, which decreases the nucleation rate and increases the growth rate.

From a processing standpoint, final particle size can be influenced by controlling initial reactant concentrations, crystallizing species concentration (supersaturation) and mixing conditions.

It is observed in the practice of the present invention that increasing the concentration of the rare-earth dopant decreases the size of the particle produced according to the present invention. As a general guideline, preparation of nano-scale particles is beneficially accomplished by employing reactant concentrations of >0.01N, preferably in the range of 0.1N to 0.8N, while preparation of micro-scale particles is beneficially accomplished by employing reactant concentrations of <0.01N. Nano-scale particles may beneficially be prepared by direct mixing of the precursor solutions as in a T-mixer or by some other form of direct mixing. In these cases the local supersaturation is high resulting in high nucleation rates, low growth rates and nano-scale particles. While micro-scale particles can also be prepared by direct mixing of highly dilute solutions, it is more convenient to combine ca. 1N solutions of the reactants in a well-stirred aqueous bath that provides a dilution factor of ca. 100-200 times—for example combining 1 liter of 2N of each alkaline earth chloride, and the appropriate amount of EuCl₃, and NH₄F in 120 liters of well-stirred water has been found to be satisfactory for preparing micro-scale particles. In these cases the local supersaturation is low resulting in low nucleation rates, high growth rates and micron size scale particles. It is important to stir the reaction vessel to effectively reduced the local supersaturation.

For the production of nano-scale particles, it is convenient to combine the reactants in a T-mixer on a continuous or semi-continuous basis. Reaction is essentially instantaneous, with nano-particulate precipitate forming in the output leg of the T as the reaction stream flows into the collector vessel. For production of micro-scale particles, the highly diluted ingredients, with concentrations of <0.01N, may need to be allowed to stand and react while being stirred for about 30 minutes. The pH of the reaction mixture is preferably maintained close to neutral, but a pH range from about 1 to 11 is acceptable.

Following reaction, the product may be conveniently separated by centrifugation and decanting of the supernatant liquid. The isolated “wet cake” so produced may then be redispersed in water (or organic solvents by a solvent exchange process) by mixing with liquid and subjecting the mixture to ultrasonic agitation for a period of 5-30 minutes. The dispersed particles are then in form well-suited to use in coatings and the like. For dispersion in non-polar solvents, it may be required to combine the particles produced with surfactants, as taught in the art.

Other suitable methods of separating the precipitate include ion exchange, dialysis and electrodialysis substantially eliminates all salts produced in the process. Further methods, to separate and concentrate the sample, include evaporation of water, centrifugation, ultrafiltration, electrodecantation. A preferred procedure is to employ ion exchange resins to remove soluble salt residues followed by evaporation to concentrate the colloidal sol produced.

It is preferred that the particles so prepared be subject to water washing in order to remove any residual water soluble starting materials. Dispersing in water followed by centrifugation is one effective method.

The resulting particles exhibit luminescence when subject to suitable optical excitation. It has been found that thermal post-treatment to about 200° C. to 1000° C. may alter certain luminescent properties, in some cases, enhancing luminosity or lifetime.

When a composition comprising a rare-earth-doped solid-state solution of alkaline earth fluorides represented by the chemical formula

RE_(x)(Ca_(a)Sr_(b)Ba_(c))_(1−x)F_(2+x−2y)O_(y)

wherein RE represents a three-valent rare-earth element, 0.005≦x≦0.20, and 0≦y≦0.2, a+b+c=1, with the proviso at least two of a, b, and c are not equal to zero, that has been synthesized at a temperature below about 100° C., is heated in the presence of oxygen in the temperature range from 200-1000° C., it gives rise to a family of novel rare-earth-doped alkaline earth fluorides that differ from one another in their luminescence peak intensity ratios. Each member of any said family exhibits a luminescence spectrum having a plurality of luminescence peaks at characteristic wavelengths. At least one pair of said luminescence peaks exhibits an intensity ratio that differs by at least 5% from the corresponding intensity ratio of the corresponding reference composition, described supra.

It has been observed that upon heating in the presence of oxygen a rare-earth doped solid state solution of alkaline earth fluorides suitable for use herein to a temperature in the range of 200-1000° C., the value of y is observed to increase.

Every member of each such family of compositions exhibits a luminescence spectrum having a plurality of luminescence peaks at characteristic wavelengths. For each family of compositions according to the present invention, there exists at least one pair of the peaks, the relative intensities of which changes depending upon the temperature/time profile to which the as-precipitated composition, described supra, is subject. The heated compositions are characterized by at least one peak intensity ratio that differs by at least 5% from the corresponding peak intensity ratio of the corresponding reference composition.

For the purposes of the present invention, a family of compositions is one in which all members thereof have the same rare-earth element at the same concentration, x, the same alkaline earth elements at the same concentrations, fluorine and oxygen, and wherein members are usually differentiated from one another by the value of y as well as by the relative peak intensity ratio of at least one pair of luminescence peaks.

Suitable means for heating include but are not limited to pressure vessel heating of an aqueous dispersion (so-called hydrothermal heating), electrical resistance furnaces, oil baths, electrically heated crucibles: liquid metal baths; lasers, radio frequency induction furnaces, microwave cavities, gas fired furnaces, oil fired furnaces, solar furnaces. Preferred is an electrical resistance furnace. Typically, when heated in a bath, the as-synthesized powder is sealed in a pressure vessel of sufficient volume to leave a head-space comprising oxygen followed by immersion of the heated tube into the heating bath. When the as-synthesized powder is subject to oven or furnace heating it can be heated in an open crucible.

It has been found satisfactory to heat the rare-earth doped solid state solution of alkaline earth fluorides suitable for use herein gradually to the desired final temperature such as by placing the specimen to be heated into a furnace at room temperature, and then heating to the desired end-point at a rate of 2-10 C.°/minute, preferably 4-6 C.°/min.

Heating is effected in the presence of oxygen. There are many potential sources for the oxygen. Heating can be effected in the air, or in an oxygen atmosphere. It is also possible for oxygen to be devolved from species employed or derived from the synthesis environment such as nitrates or hydroxyls. It is believed that even small amounts of oxygen contamination can be sufficient to effect the process.

It is found that the particles of starting material undergo some degree of sintering or agglomeration during heating, particularly at the higher temperatures in the temperature range. Depending upon the particular exigencies of the end use intended, it can be desirable to subject the product of the process to a means for comminution to smaller size. So called media milling is one such method for reducing and/or homogenizing the particle size. Numerous other methods are known in the art.

The rare-earth-doped solid state solutions of alkaline earth fluorides hereof can be combined with other ingredients to form compositions suitable for use as coatings or inks. In one embodiment, a composition is incorporated into an ink composition suitable for printing. In another embodiment, the composition hereof is incorporated into a paint composition which can be applied by any method known in the art including by brushing, rolling, or spraying.

Numerous chemical formulations are known in the art for preparing inks, paints, and other coating compositions. Every such composition in the art that contains inorganic pigments in particulate form can be employed to formulate an ink, paint, or other coating composition with the particulate luminescent composition hereof serving as the pigment. The rare-earth doped solid state solution of alkaline earth fluorides suitable for use herein may serve as the only pigment, or it may be combined with other pigments and particulate matter such as is known in the art of inks and coatings.

In one formulation, an embodiment of the rare-earth doped solid state solution of alkaline earth fluorides suitable for use herein is incorporated into an ink or coating with no other pigment, thereby resulting in a luminescent coating that after application to the surface of an article is largely invisible to the eye until subject to UV excitation of luminescence.

For the purposes of the present invention, the term “carrier matrix” refers to a continuous medium within which the particulate luminescent composition hereof is dispersed. The carrier matrix can comprise a liquid, a polymer or both.

In one embodiment, the present invention provides a composition comprising a carrier matrix and a particulate luminescent composition dispersed therein, the particulate luminescent composition comprising a rare-earth-doped solid-state solution of alkaline earth fluorides represented by the chemical formula

RE_(x)(Ca_(a)Sr_(b)Ba_(c))_(1−x)F_(2+x−2y)O_(y)

wherein RE represents a three-valent rare-earth element, 0.005≦x≦0.20, and 0≦y≦0.2, a+b+c=1, with the proviso at least two of a, b, and c are not equal to zero; the particulate luminescent composition exhibiting a luminescence spectrum having a plurality of intensity peaks at characteristic wavelengths; and wherein the carrier matrix comprises a liquid. This embodiment represents a coating composition such as an ink suitable for, e.g., printing onto the surface of an article to be marked for identification purposes.

In a further embodiment thereof, the carrier matrix further comprises a polymer. In a still further embodiment thereof, the polymer is dissolved in the liquid; that is, the carrier matrix is a polymer solution.

In another embodiment, the present invention provides a composition comprising a carrier matrix and a particulate luminescent composition dispersed within the carrier matrix, the particulate luminescent composition comprising a rare-earth-doped solid-state solution of alkaline earth fluorides represented by the chemical formula

RE_(x)(Ca_(a)Sr_(b)Ba_(c))_(1−x)F_(2+x−2y)O_(y)

wherein RE represents a three-valent rare-earth element, 0.005≦x≦0.20, and 0≦y≦0.2, a+b+c=1, with the proviso at least two of a, b, and c are not equal to zero; the particulate luminescent composition exhibiting a luminescence spectrum having a plurality of intensity peaks at characteristic wavelengths; and wherein the carrier matrix consists essentially of a polymer. This embodiment represents the composition of the invention in the form of a dried coating comprising a polymer binder and the particulate luminescent composition dispersed therein.

In a further embodiment, at least one pair of the intensity peaks in the luminescence spectrum of the particulate luminescent compound exhibits an intensity ratio with respect to one another that differs by at least 5% from the corresponding intensity ratio of the corresponding reference composition.

Additional ingredients such as electrolytes, humectants, and other additives also can be present without substantively altering the operability of the invention.

In one embodiment of the particulate luminescent composition, RE is Eu⁺³. In another embodiment, RE is Tb⁺³. In still another embodiment, RE is Er⁺³. In one embodiment of the composition of the invention, a=0, in another embodiment, b=0, and in a third embodiment, c=0. Preferably c=0. In one embodiment of the composition of the invention 0.01≦x≦0.10. More specifically, in one embodiment x=0.02. In another embodiment of the composition of the present invention, x=0.05. In still another embodiment x=0.10.

The specific wavelengths of the peaks from which the at least one peak intensity ratio is determined for any particular particulate luminescent composition depend upon the specific rare-earth element employed, and to a lesser degree to the host lattice. However, all the particulate luminescent compositions exhibit the same differentiating characteristic regarding peak intensity ratio changes.

The composition of the invention is not limited by the manner in which it is prepared or the specific form thereof. Broadly, the composition of the invention is a composition suitable for use in the preparation of a coating on a substrate. The coating so produced can be of any form. It can be in the form of a pattern such as printed text or other images, or it can be a coating of uniform thickness and appearance over a large area, such as a painted wall. While it is anticipated that the composition of the invention will find its greatest utility in the area of security markers or anti-counterfeiting, the composition can be employed for any purpose. For example, spray-coating or dip-coating exterior or interior automobile parts to create unusual visual effects in the appearance of the car.

Suitable carrier liquids include but are not limited to water, alkanes such as hexane; alcohols; aldehydes; ketones; ethers, such as dipropylene glycol monomethyl ether; esters, such as ethyl acetate, propyl acetate, or dipropylene glycol monomethyl ether acetate; nitrites, amides, aromatics such as toluene; and mixtures thereof. Water and alcohols are preferred. In one embodiment, methanol, ethanol, propanols, butanols, or mixtures thereof are employed. In another embodiment, water is employed. In a further embodiment, a mixture of alcohol and water is used as the carrier liquid.

In an ink embodiment according to the invention, the carrier liquid is used in an amount of from about 15% by weight to about 90% by weight, preferably in an amount of from about 30% by weight to about 60% weight of the composition.

The coating compositions of the present invention to be useful exhibit a desirable balance among viscosity, solubility, compatibility of components, and wettability of the substrate. When the coating composition is an ink useful in printing operations, electrostatic ink deposition methods require that resistivity and polarizability also be considered. Further, coatings of the present invention, especially inks, are quick-drying and smear resistant, and resist abrasion.

Useful polymers for systems in which the carrier liquid is aqueous include, but are not limited to poly(ethylene oxide)s, poly(acrylamide)s, poly(vinylpyrrolidone)s, poly(vinyl alcohol)s and poly(vinyl acetate)s. Included in each of these terms are both homo- and copolymers of the primary monomers, as well as mixtures thereof.

Useful polymers for use in carrier liquids based upon “hydrocarbon solvents” include, but are not limited to cellulosic polymers, poly(alpha-olefins) where the olefins contain six or more carbon atoms when used in conjunction with non-polar solvents such as alkanes; acrylic polymers when used in conjunction with polar organic solvents such as esters, ketones, and glycol- and other ethers. Esters include but are not limited to ethyl acetate, butyl acetate, butyl cellosolve acetate; carbitol esters; ketones include but are not limited to acetone, methylethylketone, diisopropylketone, and cyclohexanone. Ethers include but are not limited to tetrahydrofuran, dioxane, tetrahydrofurfural alcohol,

Other useful solvents falling outside these classes include terpineol, toluene, xylene, dimethylformamide, pyridine, ethylbenzene, carbon disulfide, 1-nitropropane, and tributylphosphate.

Mixtures of polymers are also suitable. Mixtures of polymers often provide a more desirable combination of properties than can be obtained from a single polymer.

Preferably the polymer is soluble in the carrier liquid. However, the polymer can be present as a dispersion in the carrier liquid as well.

One fundamental requirement for the polymer employed herein is that the polymer can not exhibit significant absorbance at either the excitation or emission wavelengths of interest because of interference with the intensity of the observed luminescence.

In an ink embodiment of the present invention, the polymer is employed in an amount of from 0% to about 15% by weight of the ink composition, preferably, about 2% to about 10%. Excessive amount of the polymer can adversely affect the viscosity of the ink composition.

For some printing applications, such as xerography and ink jet, electrical resistivity can be an important property. In those applications, the composition of the present invention can further comprise an electrolyte to obtain the desired electrical resistivity of the jet ink composition. Any suitable electrolyte known to those of ordinary skill in the art can be used. Suitable electrolytes include but are not limited to alkali and alkaline earth metal salts such as lithium nitrate, lithium chloride, lithium thiocyanate, sodium chloride, potassium chloride, potassium bromide, calcium chloride, and the like, and amine salts such as ammonium nitrate, ammonium chloride, dimethylamine hydrochloride, hydroxylamine hydrochloride, and the like. It is important that the electrolyte salt not interfere with the luminescence.

The electrolyte is preferably present in the ink composition in the range of from about 0.1% to about 2%, more preferably 0.4% to 0.6%, by weight of the ink composition.

The composition of the present invention can further comprise a pH adjusting agent if needed to enhance the dissolution of the binder resin, or improve compatibility with the surface. The desired pH will be dependent upon the particular solvent used and also to some extent upon the other components employed. Any suitable pH adjusting agent, acid or base, can be used so as to maintain the pH of the ink composition in the range of from about 4.0 to about 8.0, preferably in the range of from about 4.5 to about 7.5.

The ink composition of the present invention can further comprise a humectant when the liquid is water in order to prevent drying of the ink during the printing operation, as well as during storage of the ink. Humectants are hydrophilic solvents preferably having boiling points in the range of from about 150° C. to about 250° C. Any suitable humectant known to those of ordinary skill in the art can be used. Examples of suitable humectants include glycols such as ethylene glycol, propylene glycol, glycerin, diglycerin, diethylene glycol, and the like, glycol ethers such as ethylene glycol dimethyl ether, ethylene glycol diethylether, cellosolve, diethylene glycol monoethylether (Carbitol), diethylene glycol dimethylether, and diethylene glycol diethylether, dialkylsulfoxides such as dimethylsulfoxide, and other solvents such as sulfolane, N-methylpyrrolidinone, and the like. Preferred humectants include propylene glycol and diethyleneglycol monoethylether.

Any suitable amount of the humectant can be used, preferably in an amount of from about 0.5% by weight to about 5% by weight of the ink composition, and more preferably in the amount of from about 1% by weight to about 3% by weight of the ink composition. Excessive use of the humectant is to be avoided because it will increase the toxicity and/or the viscosity of the ink.

The ink composition of the present invention can further comprise a suitable biocide to prevent growth of bacteria, mold or fungus. Any suitable biocide can be used. DOWICIL™ 150, 200, and 75, benzoate salts, sorbate salts, and the like, methyl p-hydroxybenzoate, and 6-acetoxy-2,2-dimethyl-1,3-dioxane are examples of suitable biocides. The biocide can be present in the ink of the instant invention in the range of from about 0.05% by weight to about 0.5% by weight, preferably in the amount of from about 0.1% by weight of to about 0.3% by weight of the jet ink composition.

The ink composition of the present invention can further comprise a defoamer to prevent foaming of the ink during its preparation, as well as during the printing operation. Any suitable defoamer known to those of ordinary skill in the art can be used, preferably those that are miscible with the liquid. Suitable defoamers include silicone defoamers and acetylenic defoamers. The amount used is preferably in the range of from about 0.01% by weight to about 1% by weight of the ink composition, and more preferably in the range of from about 0.05% by weight to about 0.35% by weight of the ink composition. The weight percentages given above refer to that of the active ingredient, and if the defoamer is sold in a diluted form, the amount of the diluted defoamer used will be proportionately increased. Excessive use of the defoamers is to be avoided because it can adversely affect the print quality such as adhesion to the coated substrate.

The ink composition of the present invention can be printed on any suitable substrate including papers, including coated papers, plastics, leather goods, fabrics, polymeric films, glass, ceramics, metals, and so forth.

To prepare an ink suitable for use in this invention, the particulate luminescent composition can be dispersed in the carrier liquid using a media mill, sand mill, high speed disperser, mulling plates or other means known in the art. The dispersion so produced should contain 10%-70% by weight, preferably 40%-60% by weight, of the particulate luminescent composition. A dispersing aid can be added equal to ½ to 1/10, preferably ¼ to ⅕, the weight of the particles, and the remainder should be the liquid carrier or mixture of suitable liquids. When milling or mulling, dispersion and comminution occur simultaneously.

In general, a preferred ink formulation is prepared by combining a liquid carrier, a polymeric binder soluble therein, and the particulate luminescent composition so that the resulting composition contains 10-70% by weight, preferably 40-60%, of the particles, 0-15% by weight, preferably 2-10%, of polymer dissolved in the solvent, and 15-90%, preferably 30-60% by weight of the carrier liquid. Optionally the composition can contain plasticizer of 0 to 5% and dispersant of 0 to 8%. The ingredients can be combined in any order. The polymer can first be dissolved in the solvent followed by addition of the particulate material which is then dispersed therein; the particulate material so added can be in the form of dry particles or a pre-prepared particle dispersion. Alternatively, the particle dispersion can be prepared first followed by addition and dissolution of the polymer.

Varnishes according to the present invention may be formulated by adapting conventional methods known in the art. In a typical formulation, the particulate luminescent compound is combined in a viscous polymer solution consisting of ca. 10% of a fugitive solvent. Varnishes are conventionally applied by brushing, rolling, and spraying.

Further provided is a process comprising contacting a surface with a composition comprising a carrier liquid, and a particulate luminescent composition dispersed therein. The particulate luminescent composition comprising a rare-earth-doped solid-state solution of alkaline earth fluorides represented by the chemical formula

RE_(x)(Ca_(a)Sr_(b)Ba_(c))_(1−x)F_(2+x−2y)O_(y)

wherein RE represents a three-valent rare-earth element, 0.005≦x≦0.20, and 0≦y≦0.2, a+b+c=1, with the proviso at least two of a, b, and c are not equal to zero; the particulate luminescent composition exhibiting a luminescence spectrum having a plurality of intensity peaks at characteristic wavelengths; thereby forming upon the surface a coating comprising the composition; and, extracting the carrier liquid from the coating.

In a further embodiment of the process of the invention, at least one pair of the intensity peaks in the luminescence spectrum of the particulate luminescent compound exhibits an intensity ratio with respect to one another that differs by at least 5% from the corresponding intensity ratio of the corresponding reference composition.

According to the process of the invention, the composition of the invention can be applied to a surface in any manner consistent with the viscosity and specific constitution of the composition, and suitable for the particular surface to be coated. The composition can be applied in the form of a paint: brushed on, rolled on, or sprayed on. An article can be dip-coated into the composition, or the composition can be applied to a substrate by solution casting and drawn-down, or melt-casting. All such methods are well-known in the art.

In one embodiment of the particulate luminescent composition, RE is Eu⁺³. In another embodiment, RE is Tb⁺³. In still another embodiment, RE is Er⁺³. In one embodiment of the composition of the invention, a=0, in another embodiment, b=0, and in a third embodiment, c=0. Preferably c=0. In one embodiment of the composition of the invention 0.01≦x≦0.10. More specifically, in one embodiment x=0.02. In another embodiment of the composition of the present invention, x=0.05. In still another embodiment x=0.10.

The specific wavelengths of the peaks from which the at least one peak intensity ratio is determined for any particular particulate luminescent composition depend upon the specific rare-earth element employed, and to a lesser degree to the host lattice. However, all the particulate luminescent compositions exhibit the same differentiating characteristic regarding peak intensity ratio changes.

Suitable carrier liquids include but are not limited to water, alkanes such as hexane; alcohols; aldehydes; ketones; ethers, such as dipropylene glycol monomethyl ether; esters, such as ethyl acetate, propyl acetate, or dipropylene glycol monomethyl ether acetate; nitrites, amides, aromatics such as toluene; and mixtures thereof. Water and alcohols are preferred. In one embodiment, methanol, ethanol, propanols, butanols, or mixtures thereof are employed. In another embodiment, water is employed. In a further embodiment, a mixture of alcohol and water is used as the carrier liquid.

Other useful solvents falling outside these classes include terpineol, toluene, xylene, dimethylformamide, pyridine, ethylbenzene, carbon disulfide, 1-nitropropane, and tributylphosphate.

In one embodiment, the process of the invention is a printing process wherein the composition employed therein is an ink wherein the carrier liquid is used in an amount of from about 15% by weight to about 90% by weight, preferably in an amount of from about 30% by weight to about 60% weight of the composition.

Useful polymers for aqueous inks suitable for use in the printing embodiment of the process of the present invention include, but are not limited to poly(ethylene oxide)s, poly(acrylamide)s, poly(vinylpyrrolidone)s, poly(vinyl alcohol)s and poly(vinyl acetate)s. Included in each of these terms are both homo- and copolymers of the primary monomers, as well as mixtures thereof.

Useful polymers for non-aqueous inks suitable for use in the printing embodiment of the process of the present invention include, but are not limited to cellulosic polymers, poly(alpha-olefins) where the olefins contain six or more carbon atoms when used in conjunction with non-polar solvents such as alkanes; acrylic polymers when used in conjunction with polar organic solvents such as esters, ketones, and glycol- and other ethers. Esters include but are not limited to ethyl acetate, butyl acetate, butyl cellosolve acetate; carbitol esters; ketones include but are not limited to acetone, methylethylketone, diisopropylketone, and cyclohexanone. Ethers include but are not limited to tetrahydrofuran, dioxane, tetrahydrofurfural alcohol.

Mixtures of polymers are also suitable. Mixtures of polymers often provide a more desirable combination of properties than can be obtained from a single polymer. Preferably the polymer is soluble in the carrier liquid. However, the polymer can be present as a dispersion in the carrier liquid as well.

One fundamental requirement for the polymer employed herein is that the polymer can not exhibit significant absorbance at either the excitation or emission wavelengths of interest because of interference with the intensity of the observed luminescence.

In an ink suitable for use in the printing embodiment of the process of the present invention, the polymer is employed in an amount of from 0% to about 15% by weight of the ink composition, preferably, about 2% to about 10%. Excessive amount of the polymer can adversely affect the viscosity of the ink composition.

For some printing applications, such as xerography and ink jet, electrical resistivity can be an important property. In those applications, a suitable ink can further comprise an electrolyte to obtain the desired electrical resistivity particularly of an ink-jet composition. Any suitable electrolyte known to those of ordinary skill in the art can be used. Suitable electrolytes include but are not limited to alkali and alkaline earth metal salts such as lithium nitrate, lithium chloride, lithium thiocyanate, sodium chloride, potassium chloride, potassium bromide, calcium chloride, and the like, and amine salts such as ammonium nitrate, ammonium chloride, dimethylamine hydrochloride, hydroxylamine hydrochloride, and the like. It is important that the electrolyte salt not interfere with the luminescence.

The electrolyte is preferably present in the ink in the range of from about 0.1% to about 2%, more preferably 0.4% to 0.6%, by weight of the ink composition.

An ink suitable for use in the printing embodiment of the process of the present invention can include a pH adjusting agent if needed to enhance the dissolution of the binder resin, or improve compatibility with the surface to be printed on. The desired pH will be dependent upon the particular solvent used and also to some extent upon the other components employed. Any suitable pH adjusting agent, acid or base, can be used so as to maintain the pH of the ink composition in the range of from about 4.0 to about 8.0, preferably in the range of from about 4.5 to about 7.5.

An ink suitable for use in the printing embodiment of the process of the present invention can include a humectant when the liquid is water in order to prevent drying of the ink during the printing operation, as well as during storage of the ink. Humectants are hydrophilic solvents preferably having boiling points in the range of from about 150° C. to about 250° C. Any suitable humectant known to those of ordinary skill in the art can be used. Examples of suitable humectants include glycols such as ethylene glycol, propylene glycol, glycerin, diglycerin, diethylene glycol, and the like, glycol ethers such as ethylene glycol dimethyl ether, ethylene glycol diethylether, cellosolve, diethylene glycol monoethylether (Carbitol), diethylene glycol dimethylether, and diethylene glycol diethylether, dialkylsulfoxides such as dimethylsulfoxide, and other solvents such as sulfolane, N-methylpyrrolidinone, and the like. Preferred humectants include propylene glycol and diethyleneglycol monoethylether.

Any suitable amount of the humectant can be used, preferably in an amount of from about 0.5% by weight to about 5% by weight of the ink composition, and more preferably in the amount of from about 1% by weight to about 3% by weight of the ink composition. Excessive use of the humectant is to be avoided because it will increase the toxicity and/or the viscosity of the ink.

An ink suitable for use in the printing embodiment of the process of the present invention can include a suitable biocide to prevent growth of bacteria, mold or fungus. Any suitable biocide can be used. DOWICIL™ 150, 200, and 75, benzoate salts, sorbate salts, and the like, methyl p-hydroxybenzoate, and 6-acetoxy-2,2-dimethyl-1,3-dioxane are examples of suitable biocides. The biocide can be present in the ink of the instant invention in the range of from about 0.05% by weight to about 0.5% by weight, preferably in the amount of from about 0.1% by weight of to about 0.3% by weight of the jet ink composition.

An ink suitable for use in the printing embodiment of the process of the present invention can include a defoamer to prevent foaming of the ink during its preparation, as well as during the printing operation. Any suitable defoamer known to those of ordinary skill in the art can be used, preferably those that are miscible with the liquid. Suitable defoamers include silicone defoamers and acetylenic defoamers. The amount used is preferably in the range of from about 0.01% by weight to about 1% by weight of the ink composition, and more preferably in the range of from about 0.05% by weight to about 0.35% by weight of the ink composition. The weight percentages given above refer to that of the active ingredient, and if the defoamer is sold in a diluted form, the amount of the diluted defoamer used will be proportionately increased. Excessive use of the defoamers is to be avoided because it can adversely affect the print quality such as adhesion to the coated substrate.

Printing can be effected on any suitable substrate including papers, including coated papers, plastics, leather goods, fabrics, polymeric films, glass, ceramics, metals, and so forth.

To prepare a suitable ink the particulate luminescent composition can be dispersed in the carrier liquid using a media mill, sand mill, high speed disperser, mulling plates or other means known in the art. The dispersion so produced should contain 10%-70% by weight, preferably 40%-60% by weight, of the particulate luminescent composition. A dispersing aid can be added equal to ½ to 1/10, preferably ¼ to ⅕, the weight of the particles, and the remainder should be the liquid carrier or mixture of suitable liquids. When milling or mulling, dispersion and comminution occur simultaneously.

In general, an ink formulation is prepared by combining a liquid carrier, a polymeric binder soluble therein, and the particulate luminescent composition so that the resulting composition contains 10-70% by weight, preferably 40-60%, of the particles, 0-15% by weight, preferably 2-10%, of polymer dissolved in the solvent, and 15-90%, preferably 30-60% by weight of the carrier liquid. Optionally the composition can contain plasticizer of 0 to 5% and dispersant of 0 to 8%. The ingredients can be combined in any order. The polymer can first be dissolved in the solvent followed by addition of the particulate material which is then dispersed therein; the particulate material so added can be in the form of dry particles or a pre-prepared particle dispersion. Alternatively, the particle dispersion can be prepared first followed by addition and dissolution of the polymer.

Further provided according to the present invention is an article having a surface, the surface having disposed upon it a coating comprising a particulate luminescent composition, the particulate luminescent composition comprising a rare-earth-doped solid-state solution of alkaline earth fluorides represented by the chemical formula

RE_(x)(Ca_(a)Sr_(b)Ba_(c))_(1−x)F_(2+x−2y)O_(y)

wherein RE represents a three-valent rare-earth element, 0.005≦x≦0.20, and 0≦y≦0.2, a+b+c=1, with the proviso at least two of a, b, and c are not equal to zero, the particulate luminescent composition exhibiting a luminescence spectrum having a plurality of intensity peaks at characteristic wavelengths.

In a further embodiment of the article of the invention, at least one pair of the intensity peaks in the luminescence spectrum of the particulate luminescent compound exhibits an intensity ratio with respect to one another that differs by at least 5% from the corresponding intensity ratio of the corresponding reference composition.

In one embodiment of the particulate luminescent composition, RE is Eu⁺³. In another embodiment, RE is Tb⁺³. In still another embodiment, RE is Er⁺³. In one embodiment of the composition of the invention, a=0, in another embodiment, b=0, and in a third embodiment, c=0. Preferably c=0. In one embodiment of the composition of the invention 0.01≦x≦0.10. More specifically, in one embodiment x=0.02. In another embodiment of the composition of the present invention, x=0.05. In still another embodiment x=0.10, and in a still further embodiment, x=0.20.

The specific wavelengths of the peaks from which at least one peak intensity ratio is determined for any particular particulate luminescent composition depend upon the specific rare-earth element employed, and to a lesser degree to the host lattice However, all the particulate luminescent compositions exhibit the same differentiating characteristic regarding peak intensity ratio changes.

In a further embodiment, the coating further comprises a polymer within which the particles of the particulate luminescent composition is dispersed, the polymer adhering to the surface of the article. Conventionally, a polymer serving that function is known as a binder polymer or binder resin.

Useful polymers for use in the article of the present invention include, but are not limited to poly(ethylene oxide)s, poly(acrylamide)s, poly(vinylpyrrolidone)s, poly(vinyl alcohol)s and poly(vinyl acetate)s. Included in each of these terms are both homo- and copolymers of the primary monomers. Also included are cellulosic polymers, poly(alpha-olefins) where the olefins contain six or more carbon atoms, acrylic polymers.

Mixtures of polymers are also suitable. Mixtures of polymers often provide a more desirable combination of properties than can be obtained from a single polymer.

One fundamental requirement for the polymer employed herein is that the polymer can not exhibit significant absorbance at either the excitation or emission wavelengths of interest because of interference with the intensity of the observed luminescence.

A coating composition according to the article of the invention can further comprise an electrolyte, a humectant, a pH adjusting agent, a defoamer, a plasticizer, a biocide, a dispersing aid or such other adjuvants that are commonly employed in the art of formulating inks and paints.

In general, a suitable coating for the article of the invention comprises 100 to 70 parts by weight of the particulate luminescent composition suitable for use herein, and 0 to 20 parts by weight of a suitable polymer. Optionally the composition can contain as much as circa 20 parts by weight of such other adjuvants as are recited above.

The articles comprise any coatable surface, preferably any printable surface. Suitable coatable surfaces include but are not limited to metallic surfaces, such as automobile body parts, coins, paneling, and the like; ceramic surfaces, including glazed surfaces; glass; stone such as marble; molded plastic and fiberglass as in electronics housings and circuit boards, molded sheeting, polymeric films and the like; leather goods; fabrics; including textile goods, canvas, and the like; papers, including coated papers, including currencies, bonds, and other securities, contracts and the like.

EXAMPLES General Method Luminescence Spectra

The data are collected with a SPEX JY spectrofluorimeter equipped with the phosphorimeter option. The excitation wavelength is 394 nm (10 nm bandpass) and the pulsewidth is nominally 80 microseconds. Spectra are collected at 5 nm resolution with a 0.1 msec time delay after the excitation pulse to permit background fluorescence from the label substrates to decay. A 405 nm long-pass filter is used before the emission monochromator to eliminate second-order excitation light. Each spectrum is the average of 150 scans, each collected with one excitation pulse per 1 nm wavelength step. The detection time window is 10 msec.

Example 1

2.177 g of CaCl₂.2H₂O (Sigma-Aldrich, 99.9%), 11.838 g of SrCl₂.6H₂O (Sigma-Aldrich, 99.9%) and 0.44 g of EuCl₃.6H₂O (Sigma-Aldrich, 99.9%) were stirred into 150 ml of deionized water in a polycarbonate Erlenmeyer flask for about 5 minutes to ensure dissolution of the solids.

Separately, 4.489 g of NH₄F (Alfa Aesar, ASC reagent 99%) was dissolved by stirring into a further 150 ml aliquot of deionized water for about 5 minutes to ensure dissolution of the solids.

The prepared solutions were simultaneously but separately fed by a peristaltic pump at 10 ml/min through silicone rubber tubing into the two arms of a plastic tee (T). Teflon® tubing ran from the leg or output branch of the T into the product flask. A precipitate formed within the output branch of the T immediately beyond the point at which the two streams merged, forming a suspension in the water. The suspension formed was discharged into the product flask. During the discharge the flask containing the product suspension was stirred by magnetic stirring. After discharge was complete, the suspension was held static for about 24 hrs at ambient temperature. The resulting suspension was then centrifuged (Sorvall RC5C, Thermo Electron Corp.) at a relative centrifugal force of 9500×g for 40 min, and the supernatant (containing soluble salts) decanted and discarded. The residue was redispersed in a fresh aliquot of about 300 ml of deionized water using ultrasonic agitation (Sonics and Materials, Inc, Danbury, Conn.) at 50 W/cm². The resulting dispersion was again centrifuged and the supernatant again decanted and discarded.

The washed as precipitated powder residue was dried in a laboratory drying oven at 60° C. in air for 24 hrs to form about 15 g of a dry powder compact The oven dried powder compact was then hand-ground in a mortar and pestle to from a uniform dry powder.

A 15 g aliquot of each of the washed as precipitated powders was redispersed in about 100 ml of deionized water using ultrasonic agitation. The washed 100 ml suspension was placed in a 100 ml screw cap flexible-walled Teflon® bottle. The bottle was filled right to the brim before placing the cap on in order to exclude air. The Teflon® container containing the suspension was placed in a stainless steel pressure reactor (filled with water) and heated for 6 hrs at 245° C. at a saturated vapor pressure of 568 psi. The resulting hydrothermally treated suspension was then centrifuged and decanted as described above. The wet powder residue was dried in a laboratory drying oven at 60° C. in air for 24 hrs to form a dry powder compact. The oven dried powder compact was then hand-ground in a mortar and pestle to from a uniform dry powder.

The fired powder is hand ground using a mortar and pestle, then placed into a ceramic jar mill with ½″ milling media. Isopropyl alcohol is added to fill the mill to approx. ⅔ full. The slurry is milled overnight. The milled slurry is placed into a disposable filter and the isopropyl alcohol is filtered off leaving the milled particles in the filter. The particles are air dried for 8 hrs. then placed in a 70 C oven to complete the drying process overnight.

Approximately 1.5 g of the powder as prepared is combined with approximately 1 g of a solution of 10% ethyl cellulose and 90% 1-methyl-4-(1-methylvinyl)cyclohexanol (β-terpineol) on the bottom glass plate of a model M-5 Hoover Auto Muller (Hoover Color Corp., Irvingto, N.J.). Two pressure weight plates provided therewith are set in place over the combination and locked into place. Twenty rotations are performed after which the sample is re-spread on the glass plate using a spatula. 4-5 more cycles of twenty rotations are performed, in between each the sample is re-spread with the spatula. The final product is a highly viscous paste.

The prepared paste is screen-printed onto a commercially available Ink Jet Label (Avery Dennison Corp.) label stock using a 325 mesh screen in a Series L-400 screen printer (Engineered Technical Products, Somerville, N.J.). Three coats are applied to the label, to yield a coating weight of approximately 3-6 mg/cm² of the particulate luminescent compound in the screen-printed film. The film is heated to 110-125° C. for 10 minutes to evaporate any residual solvent.

The luminescence intensity ratio is then measured for the 589 nm and 610 nm emission lines for all 6 films as described supra, and is found to be 2.60

Example 2

The preparative method and materials of Examples 1-6 are repeated except that after the second ultrasonically-driven redispersion the resulting suspension is not dried, but rather the resulting suspension is placed into a Teflon® PFA container which in turn is placed into a pressure vessel, and heated to 245° C. for 6 hrs. After the heating the suspension is filtered through a 1.0 um syringe filter. The filtrate is redispersed in deionized water resulting in a suspension that is 5.73 wt % solids.

The suspension so prepared is ink jetted as 2 cm×2 cm squares onto the surface of a paper or of a Mylar® (DuPont-Teijin Films, Wilmington, Del.) film using a Jetlab II Table-Top Printing Platform (Microfab Technologies, Inc., Plano, Tex.) equipped with a 50 micron nozzle and 1 mm work distance. A single coating layer consumed 0.5 microliters/cm² which at 5.73% solids comes to a dry weight of 29.8 micrograms/cm². Coatings of up to 18 coats are prepared. The luminescence intensity ratios determined as described supra for peaks at 589 nm and 610 nm are found to be in the range of 2.60±5%. 

1. A composition comprising a carrier matrix, and a particulate luminescent composition dispersed therein, the particulate luminescent composition comprising a rare-earth-doped solid-state solution of alkaline earth fluorides represented by the chemical formula RE_(x)(Ca_(a)Sr_(b)Ba_(c))_(1−x)F_(2+x−2y)O_(y) wherein RE represents a three-valent rare-earth element, 0.005≦x≦0.20, and 0≦y≦0.2, a+b+c=1, with the proviso at least two of a, b, and c are not equal to zero; the particulate luminescent composition exhibiting a luminescence spectrum having a plurality of intensity peaks at characteristic wavelengths.
 2. The composition of claim 1 wherein at least one pair of the plurality of peaks exhibits an intensity ratio with respect to one another that differs by at least 5% from the corresponding peak intensity ratio of the corresponding reference composition.
 3. The composition of claim 1 wherein RE is Eu⁺³, Tb⁺³ or Er⁺³.
 4. The composition of claim 1 wherein c=0.
 5. The composition of claim 1 wherein 0.01≦x≦0.10.
 6. The composition of claim 2 wherein the intensity ratios differ by at least 10%.
 7. The composition of claim 1 wherein the carrier matrix comprises a liquid.
 8. The composition of claim 7 wherein the liquid is water.
 9. The composition of claim 1 wherein the carrier matrix comprises a polymer.
 10. The composition of claim 9 wherein the polymer is dissolved in the liquid.
 11. The composition of claim 9 wherein the polymer is ethyl cellulose.
 12. A process comprising contacting a surface with a composition comprising a carrier matrix, and a particulate luminescent composition dispersed therein, the particulate luminescent composition comprising a rare-earth-doped solid-state solution of alkaline earth fluorides represented by the chemical formula RE_(x)(Ca_(a)Sr_(b)Ba_(c))_(1−x)F_(2+x−2y)O_(y) wherein RE represents a three-valent rare-earth element, 0.005≦x≦0.20, and 0≦y≦0.2, a+b+c=1, with the proviso at least two of a, b, and c are not equal to zero; the particulate luminescent composition exhibiting a luminescence spectrum having a plurality of intensity peaks at characteristic wavelengths.
 13. The process of claim 12 wherein at least one pair of the plurality of peaks exhibits an intensity ratio with respect to one another that differs by at least 5% from the corresponding peak intensity ratio of the corresponding reference process.
 14. The process of claim 12 wherein RE is Eu⁺³, Tb⁺³ or Er⁺³.
 15. The process of claim 12 wherein c=0.
 16. The process of claim 12 wherein 0.01≦x≦0.10.
 17. The process of claim 13 wherein the intensity ratios differ by at least 10%.
 18. The process of claim 13 wherein the carrier matrix comprises a liquid.
 19. The process of claim 18 wherein the liquid is water.
 20. The process of claim 13 wherein the carrier matrix comprises a polymer.
 21. The process of claim 20 wherein the polymer is dissolved in the liquid.
 22. The process of claim 20 wherein the polymer is ethyl cellulose.
 23. The process of claim 12 wherein the contacting is effected by printing.
 24. The process of claim 33 wherein the printing is selected from screen printing or ink jet printing.
 25. An article having a surface, the surface having disposed upon it a coating comprising a particulate luminescent composition dispersed therein, the particulate luminescent composition comprising a rare-earth-doped solid-state solution of alkaline earth fluorides represented by the chemical formula RE_(x)(Ca_(a)Sr_(b)Ba_(c))_(1−x)F_(2+x−2y)O_(y) wherein RE represents a three-valent rare-earth element, 0.005≦x≦0.20, and 0≦y≦0.2, a+b+c=1, with the proviso at least two of a, b, and c are not equal to zero; the particulate luminescent composition exhibiting a luminescence spectrum having a plurality of intensity peaks at characteristic wavelengths.
 26. The article of claim 25 wherein at least one pair of the plurality of peaks exhibits an intensity ratio with respect to one another that differs by at least 5% from the corresponding peak intensity ratio of the corresponding reference composition.
 27. The article of claim 25 wherein the coating composition further comprises a polymer.
 28. The article of claim 25 wherein RE is Eu⁺³, Tb⁺³ or Er⁺³
 29. The article of claim 25 wherein c=0.
 30. The article of 25 wherein 0.01≦x≦0.10.
 31. The article of claim 26 wherein the intensity ratios differ by at least 10%.
 32. The article of claim 27 wherein the polymer is ethyl cellulose. 